S-Plastics Xenoy X5630 resin is Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 10 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 60 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 45 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 100 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 80 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 138 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 112 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 4.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.4E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C to 80°C, flow | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 112 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.35 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 11 | g/10 min | ASTM D 1238 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.42 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:03/05/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 265 - 275 | °C |
| Nozzle Temperature | 260 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 250 - 275 | °C |
| Rear - Zone 1 Temperature | 240 - 270 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 100 | °C |
| Source GMD, last updated:03/05/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy X5630.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|