S-Plastics Xenoy XD1507S resin is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties,
designed for self coloured, optiwall bumper facias.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | >65 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 0°C | 20 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Thermal Conductivity | 0.18 | W/m-°C | ISO 8302 |
CTE, 23°C to 80°C, flow | 1.1E-04 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 1.1E-04 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 123 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 126 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 70 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Mold Shrinkage on Tensile Bar, flow (2) | 0.8 - 1.1 | % | S-Plastics Method |
Density | 1.23 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate, MVR at 250°C/2.16 kg | 14 | cm³/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 |
Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
Source GMD, last updated:01/18/2000 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 90 - 100 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 255 - 270 | °C |
Nozzle Temperature | 250 - 265 | °C |
Front - Zone 3 Temperature | 250 - 270 | °C |
Middle - Zone 2 Temperature | 240 - 265 | °C |
Rear - Zone 1 Temperature | 230 - 250 | °C |
Hopper Temperature | 40 - 60 | °C |
Mold Temperature | 60 - 80 | °C |
Source GMD, last updated:01/18/2000 |
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
For more information please download the datasheet |
|
S-Plastics Xenoy XD1507S.pdf |
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
Click to consult and get the latest quotation within 24 hours! |