S-Plastics Xenoy X2500UV resin is an unreinforced amorphous PC+PET blend, offering excellent impact performance over a wide temperature range. It combines very good flow characteristics with high heat resistance. X2500UV has excellent dimension stability, good adhesion to PU based glues and paints, and good UV resistance.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 53 | MPa | ASTM D 638 |
| Tensile Strain, yield | 5 | % | ASTM D 638 |
| Tensile Strain, break | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2170 | MPa | ASTM D 638 |
| Flexural Stress | 79 | MPa | ASTM D 790 |
| Flexural Modulus | 2100 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| Hardness, H358/30 | 95 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 690 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 610 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 38 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 50 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, -20°C | 10 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 7 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.18 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 140 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.5 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 265°C/2.16kg | 8 | g/10 min | ASTM D 1238 |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.7 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 4 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at | 2.7 | mm | IEC 60695-2-12 |
| Source GMD, last updated:04/07/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 265 - 275 | °C |
| Nozzle Temperature | 260 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 250 - 275 | °C |
| Rear - Zone 1 Temperature | 240 - 270 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 100 | °C |
| Source GMD, last updated:04/07/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy X2500UV.pdf |
|