S-Plastics Xenoy EXXY0137 resin is iQ* (PBT+PC) resin is an environmental responsible low carbon footprint resin. It is a mineral filled PC/iQ-PBT resin developed for automotive painted doorhandles, with high strength, high ductility and good fatigue behavior.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 130 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4000 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 104 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3600 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3450 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 250 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 127 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 100 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 128 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.29 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 7 | g/10 min | ASTM D 1238 |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 9 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:04/26/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 275 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 265 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Mold Temperature | 40 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:04/26/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy EXXY0137.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|