S-Plastics Xenoy 1850 resin is PBT+PC, UV-Stabilizer, Impact Modified- restricted to Downeast
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 147 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 87 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2290 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 828 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 668 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 145 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.21 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.94 - 1 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.89 - 1 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 15.3 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:09/28/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 275 | °C |
| Nozzle Temperature | 255 - 270 | °C |
| Front - Zone 3 Temperature | 255 - 275 | °C |
| Middle - Zone 2 Temperature | 250 - 270 | °C |
| Rear - Zone 1 Temperature | 245 - 265 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:09/28/2004 | ||