S-Plastics Xenoy1403B resin is AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Blow Molding grade
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 90 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1930 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 68 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1860 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 54 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 125 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 101 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 87 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.57E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.76E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 7 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:02/12/1999 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 95 - 100 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.01 - 0.02 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature (Parison) | 240 - 250 | °C |
| Barrel - Zone 1 Temperature | 235 - 245 | °C |
| Barrel - Zone 2 Temperature | 235 - 245 | °C |
| Barrel - Zone 3 Temperature | 235 - 245 | °C |
| Barrel - Zone 4 Temperature | 235 - 245 | °C |
| Adapter - Zone 5 Temperature | 235 - 245 | °C |
| Head - Zone 6 - Top Temperature | 235 - 245 | °C |
| Head - Zone 7 - Bottom Temperature | 235 - 245 | °C |
| Mold Temperature | 65 - 90 | °C |
| Die Temperature | 240 - 250 | °C |
| Source GMD, last updated:02/12/1999 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem CRS5011.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|