Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applications
| TYPICAL PROPERTIES¹ | TYPICAL VALUE | Unit | Standard |
| MECHANICAL | |||
| Tensile Stress, yld, Type I, 50 mm/min Tensile Stress, brk, Type I, 50 mm/min |
640 420 |
kgf/cm² kgf/cm² |
ASTM D 638 ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 65 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min Flexural Stress, yld, 1.3 mm/min, 50 mm span Flexural Modulus, 1.3 mm/min, 50 mm span |
25200 900 22800 |
kgf/cm² kgf/cm² kgf/cm² |
ASTM D 638 ASTM D 790 ASTM D 790 |
| IMPACT | |||
| Izod Impact, notched, 23°C Instrumented Impact Total Energy, 23°C |
56 662 |
cm-kgf/cm cm-kgf |
ASTM D 256 ASTM D 3763 |
| THERMAL | |||
| Vicat Softening Temp, Rate B/50 | 102 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 78 | °C | ASTM D 648 |
| PHYSICAL | |||
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 26 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | |||
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.1 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VB Rating (3) | 2.5 | mm | UL 94 |
| Injection Molding | ||
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 245 - 275 | °C |
| Nozzle Temperature | 245 - 275 | °C |
| Front - Zone 3 Temperature | 245 - 275 | °C |
| Middle - Zone 2 Temperature | 220 - 265 | °C |
| Rear - Zone 1 Temperature | 220 - 255 | °C |
| Mold Temperature | 60 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy ENH2900.pdf |
|