Sabic Xenoy XL1339 resin is Data generated in BOZ labs. High heat grade for nonchemical resistance required applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2090 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2090 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | ASTM D 1044 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 699 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 672 | J/m | ASTM D 256 |
| Izod Impact, notched, -20°C | 598 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 245 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 224 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 38 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 30°C, flow | 7.56E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 7.92E-05 | 1/°C | ASTM D 696 |
| Thermal Conductivity | 0.18 | W/m-°C | ASTM C 177 |
| Vicat Softening Temp, Rate A/50 | 140 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.22 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.1 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.7 | % | ASTM D 570 |
| Water Absorption, 50% RH, equilib | 0.2 | % | ASTM D 570 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.8 | % | SABIC Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.5 - 0.8 | % | SABIC Method |
| Poisson's Ratio | 0.4 | - | ASTM D 638 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 4 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 16.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Source GMD, last updated:01/05/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 275 | °C |
| Nozzle Temperature | 255 - 270 | °C |
| Front - Zone 3 Temperature | 255 - 275 | °C |
| Middle - Zone 2 Temperature | 250 - 270 | °C |
| Rear - Zone 1 Temperature | 245 - 265 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:01/05/2000 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
Sabic Xenoy XL1339.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|