Sabic Xenoy XD1432G resin is a semicrystalline PBT-PC blend with excellent low temperature impact and high shrinkage. For solvent based painted bumpersystems.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 40 | mg/1000cy | SABIC Method |
| Tensile Stress, yield, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 150 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
| Hardness, H358/30 | 80 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 60 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 55 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 117 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 120 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 1.2 - 1.6 | % | SABIC Method |
| Mold Shrinkage on Tensile Bar, xflow (2) (5) | 1.2 - 1.6 | % | SABIC Method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:2009/08/10 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:2009/08/10 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|