S-Plastics Xenoy X5630P resin is Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4050 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 80°C, flow | 5.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:10/10/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 265 - 275 | °C |
| Nozzle Temperature | 260 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 250 - 275 | °C |
| Rear - Zone 1 Temperature | 240 - 270 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 100 | °C |
| Source GMD, last updated:10/10/2008 | ||
Other related products we recommend:
For more information please download the datasheet | |
 | S-Plastics Xenoy X5630P.pdf |