S-Plastics Xenoy X4000BM resin is UV stabilized, high melt strength grade for thermoforming, extrusion or blow molding of automotive large exterior applications. Heat Stabilized, Impact Modified, UV stabilized, Opaque
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 52 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 60 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 715 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 530 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 120 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.6E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 121 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8 - 1 | % | S-Plastics Method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Source GMD, last updated:06/16/2005 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 95 - 100 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.01 - 0.02 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature (Parison) | 240 - 250 | °C |
| Barrel - Zone 1 Temperature | 235 - 245 | °C |
| Barrel - Zone 2 Temperature | 235 - 245 | °C |
| Barrel - Zone 3 Temperature | 235 - 245 | °C |
| Barrel - Zone 4 Temperature | 235 - 245 | °C |
| Adapter - Zone 5 Temperature | 235 - 245 | °C |
| Head - Zone 6 - Top Temperature | 235 - 245 | °C |
| Head - Zone 7 - Bottom Temperature | 235 - 245 | °C |
| Mold Temperature | 65 - 90 | °C |
| Die Temperature | 240 - 250 | °C |
| Source GMD, last updated:06/16/2005 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy X4000BM.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|