S-Plastics Xenoy EXXY0160 resin is Fuel resistant, high impact strength with excellent fuel barrier properties - suitable for injection molding applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 29 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 30 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 203 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1170 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 44 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1400 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 931 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 78 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.06E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.31E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.21 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 2.2 - 2.4 | % | S-Plastics Method |
| Source GMD, last updated:03/06/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Nozzle Temperature | 240 - 255 | °C |
| Front - Zone 3 Temperature | 245 - 260 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Mold Temperature | 50 - 75 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.025 | mm |
| Source GMD, last updated:03/06/2008 | ||