S-Plastics Xenoy EXXY0085 resin is Blow Moldable Xenoy
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 38 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 180 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2100 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 70 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 60 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 58 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.23 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 1.9 - 2.2 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 15 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:11/15/2005 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 95 - 100 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.01 - 0.02 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature (Parison) | 240 - 250 | °C |
| Barrel - Zone 1 Temperature | 235 - 245 | °C |
| Barrel - Zone 2 Temperature | 235 - 245 | °C |
| Barrel - Zone 3 Temperature | 235 - 245 | °C |
| Barrel - Zone 4 Temperature | 235 - 245 | °C |
| Adapter - Zone 5 Temperature | 235 - 245 | °C |
| Head - Zone 6 - Top Temperature | 235 - 245 | °C |
| Head - Zone 7 - Bottom Temperature | 235 - 245 | °C |
| Mold Temperature | 65 - 90 | °C |
| Die Temperature | 240 - 250 | °C |
| Source GMD, last updated:11/15/2005 | ||