Send Message

Transparent S-Plastic Polyetherimide Ultem PEI Resin Pellets AUT200 Tg 217C

100KG
MOQ
*USD
Price
Transparent S-Plastic Polyetherimide Ultem PEI Resin Pellets AUT200  Tg 217C
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 337°C/6.6 Kgf: 17.8
Highlight:

Transparent Ultem PEI Resin

,

Ultem PEI Resin AUT200

,

Ultem polyethylene resin pellets

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Ultem
Certification: COA/ICP Test/Rohs/MSDS
Model Number: AUT200
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Ultem  AUT200 resin is Transparent high flow Polyetherimide (Tg 217C). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 204C (S-Plastics IP method)

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 110 MPa ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min 105 MPa ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 60 % ASTM D 638
Tensile Modulus, 5 mm/min 3590 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 165 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 3520 MPa ASTM D 790
Tensile Stress, yield, 5 mm/min 105 MPa ISO 527
Tensile Stress, break, 5 mm/min 85 MPa ISO 527
Tensile Strain, yield, 5 mm/min 6 % ISO 527
Tensile Strain, break, 5 mm/min 60 % ISO 527
Tensile Modulus, 1 mm/min 3200 MPa ISO 527
Flexural Stress, yield, 2 mm/min 160 MPa ISO 178
Flexural Modulus, 2 mm/min 3300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 1335 J/m ASTM D 4812
Izod Impact, notched, 23°C 32 J/m ASTM D 256
Izod Impact, notched, -30°C 35 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 33 J ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 5 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 5 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 3 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 219 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 205 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 197 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 199 °C ASTM D 648
CTE, -40°C to 150°C, flow 5.5E-05 1/°C ASTM E 831
CTE, -40°C to 150°C, xflow 5.5E-05 1/°C ASTM E 831
CTE, 23°C to 150°C, flow 5.E-05 1/°C ISO 11359-2
CTE, 23°C to 150°C, xflow 5.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 211 °C ISO 306
Vicat Softening Temp, Rate B/120 212 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 190 °C ISO 75/Ae
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 193 °C ISO 75/Af
Metallized Haze Onset 204 °C S-Plastics Method
PHYSICAL Value Unit Standard
Specific Gravity 1.27 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf 17.8 g/10 min ASTM D 1238
Density 1.27 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 1.25 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.7 % ISO 62
Melt Volume Rate, MVR at 360°C/5.0 kg 25 cm³/10 min ISO 1133
Source GMD, last updated:11/09/2007    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 150 °C
Drying Time 4 - 6 hrs
Drying Time (Cumulative) 24 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 350 - 400 °C
Nozzle Temperature 345 - 400 °C
Front - Zone 3 Temperature 345 - 400 °C
Middle - Zone 2 Temperature 340 - 400 °C
Rear - Zone 1 Temperature 330 - 400 °C
Mold Temperature 135 - 165 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:11/09/2007  

 

For more information please download the datasheet

Transparent S-Plastic Polyetherimide Ultem PEI Resin Pellets AUT200  Tg 217C 0  S-Plastics Ultem AUT200.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Transparent S-Plastic Polyetherimide Ultem PEI Resin Pellets AUT200  Tg 217C 1Click to consult and get the latest quotation within 24 hours!

 