S-Plastics Ultem AUR200G6 resin The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain,Water Absorption, Thermal Conductivity and Shrinkage which are typical data. The MVR of this material at 337 degrees C/6.7 kgf will have a specification between 3 and 7.5 (MFR: 4.2-10.5)
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.3 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.2 - 0.4 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 7.5 | g/10 min | ASTM D 1238 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.9 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Source GMD, last updated:2009/06/17 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Nozzle Temperature | 360 - 410 | °C |
| Front - Zone 3 Temperature | 370 - 420 | °C |
| Middle - Zone 2 Temperature | 360 - 410 | °C |
| Rear - Zone 1 Temperature | 350 - 400 | °C |
| Hopper Temperature | 80 - 120 | °C |
| Mold Temperature | 140 - 180 | °C |
| Source GMD, last updated:2009/06/17 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem AUR200G6.pdf |
|