Sabic Ultem AUT195M resin is High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method). Contains low level of mold release.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 97 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 85 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 70 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3300 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3170 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 95 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 75 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2083 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 55 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 2670 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 209 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 187 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 191 | °C | ASTM D 648 |
| Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 210 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 195 | °C | ISO 75/Be |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Af |
| Metallized Haze Onset | 195 | °C | SABIC Method |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.26 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 337°C/6.6 kgf | 24 | g/10 min | ASTM D 1238 |
| Density | 1.26 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.9 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Melt Volume Rate, MVR at 340°C/5.0 kg | 16 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:2010/08/19 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 130 - 140 | °C |
| Drying Time | 3 - 4 | hrs |
| Melt Temperature | 340 - 380 | °C |
| Nozzle Temperature | 340 - 360 | °C |
| Front - Zone 3 Temperature | 340 - 360 | °C |
| Middle - Zone 2 Temperature | 330 - 350 | °C |
| Rear - Zone 1 Temperature | 320 - 340 | °C |
| Hopper Temperature | 80 - 100 | °C |
| Mold Temperature | 125 - 140 | °C |
| Source GMD, last updated:2010/08/19 | ||
|
For more information please download the datasheet |
|
 |
Sabic Ultem AUT195M.pdf |
|