High Flow S-Plastic Ultem Pellets Polyetherimide Resin AUT195 For Automotive Lighting

100KG
MOQ
*USD
Price
High Flow S-Plastic Ultem Pellets Polyetherimide Resin AUT195 For Automotive Lighting
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 337°C/6.6 Kgf: 24
Highlight:

ultem pellets AUT195

,

Polyetherimide ultem pellets

,

Ultem polyetherimide resin

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Ultem
Certification: COA/ICP Test/Rohs/MSDS
Model Number: AUT195
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Ultem  AUT195 resin is High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (S-Plastics test method).


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 96 MPa ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 70 % ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span 145 MPa ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span 3170 MPa ASTM D 790
Tensile Modulus, 1 mm/min 3000 MPa ISO 527
Flexural Modulus, 2 mm/min 3100 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 2082 J/m ASTM D 4812
Izod Impact, notched, 23°C 53 J/m ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm 2136 J/m ASTM D 256
Izod Impact, notched 80*10*4 +23°C 5 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 5 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 190 °C ASTM D 648
Thermal Conductivity 0.23 W/m-°C ISO 8302
CTE, 23°C to 150°C, flow 6.E-05 1/°C ISO 11359-2
CTE, 23°C to 150°C, xflow 6.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/120 205 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 195 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 180 °C ISO 75/Ae
Metallized Haze Onset 195 °C S-Plastics Method
PHYSICAL Value Unit Standard
Specific Gravity 1.26 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage on Tensile Bar, xflow (2) 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf 24 g/10 min ASTM D 1238
Density 1.27 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.9 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.5 % ISO 62
Melt Volume Rate, MVR at 340°C/5.0 kg 16 cm³/10 min ISO 1133
Source GMD, last updated:2009/03/13    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 135 °C
Drying Temperature 130 - 140 °C
Drying Time 4 - 6 hrs
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 10 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 350 - 370 °C
Melt Temperature 340 - 380 °C
Nozzle Temperature 350 - 370 °C
Nozzle Temperature 340 - 360 °C
Front - Zone 3 Temperature 350 - 370 °C
Front - Zone 3 Temperature 340 - 360 °C
Middle - Zone 2 Temperature 330 - 350 °C
Middle - Zone 2 Temperature 345 - 365 °C
Rear - Zone 1 Temperature 340 - 360 °C
Rear - Zone 1 Temperature 320 - 340 °C
Hopper Temperature 80 - 100 °C
Mold Temperature 125 - 140 °C
Mold Temperature 135 - 165 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:2009/03/13  

 

For more information please download the datasheet

High Flow S-Plastic Ultem Pellets Polyetherimide Resin AUT195 For Automotive Lighting 0  S-Plastics Ultem AUT195.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

High Flow S-Plastic Ultem Pellets Polyetherimide Resin AUT195 For Automotive Lighting 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)