S-Plastics Ultem STM1600 resin is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be selfcolored and easily processed on conventional equipment. The material may also have a fit in flexible profiles or injection molded parts.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 40 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 10 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 64 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1400 | MPa | ASTM D 638 |
| Flexural Stress | 48 | MPa | ASTM D 790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 48 | MPa | ASTM D 790 |
| Flexural Modulus | 1250 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1250 | MPa | ASTM D 790 |
| Hardness, Shore D | 72 | - | ASTM D 2240 |
| Taber Abrasion, CS-17, 1 kg | 50 | mg/1000cy | ASTM D 1044 |
| Tensile Stress, yield, 50 mm/min | 42 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 41 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 10 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 74 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1380 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 55 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1250 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 412 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 36 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 167 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Bf |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.86 - 1.01 | % | S-Plastics Method |
| Melt Flow Rate, 295°C/6.6 kgf | 8.6 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.58 | % | ISO 62-1 |
| Water Absorption, (23°C/sat) | 0.58 | % | ISO 62 |
| Matrix Tg | 195 | °C | DMA |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+16 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 16.6 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.14 | - | ASTM D 150 |
| Relative Permittivity, 100 kHz | 3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.02 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.014 | - | ASTM D 150 |
| Dissipation Factor, 100 kHz | 0.0064 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.0055 | - | ASTM D 150 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Oxygen Index (LOI) | 48 | % | ASTM D 2863 |
| Source GMD, last updated:02/07/2008 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 310 - 320 | °C |
| Nozzle Temperature | 310 - 320 | °C |
| Front - Zone 3 Temperature | 310 - 320 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 105 - 115 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Parameter | ||
| Wire Coating Extrusion | Value | Unit |
| Drying Temperature | 110 - 130 | °C |
| Drying Time | 5 - 7 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 28:1 | - |
| Compression Ratio | 2.1:1 to 2.7:1 | - |
| Feed - Compression - Metering | 10 - 5 - 10 | D |
| Screw Speed | 5 - 50 | rpm |
| Feed Zone Temperature | 270 - 310 | °C |
| Middle Zone Temperatures | 280 - 320 | °C |
| Head Zone Temperature | 290 - 330 | °C |
| Neck Temperature | 290 - 330 | °C |
| Cross-head Temperature | 290 - 330 | °C |
| Die Temperature | 290 - 330 | °C |
| Melt Temperature | 290 - 330 | °C |
| Conductor Pre-heat Temperature | 100 - 150 | °C |
| Screen Pack | 100 - 200 | - |
| Water Bath Temperature | 70 - 90 | °C |
| Source GMD, last updated:02/07/2008 | ||
Available in stock with favorable price
1.1000 series
1000,MI9.0； 1010,MI18.0； Hu1000, medical grade.
2.2000 series, add GF
2100, add 10%GF, MI 7.0;
2110, add 10%GF, MI 11.0;
2200, add 20%GF, MI 6.0;
2210, add 20%GF, MI 8.4;
2300, add 30%GF, MI 5.0;
2310, add 30%GF, MI 7.6;
3. Others
MD130, MD131, AUT195, ATX200, etc;
In recent years, we have deeply cultivated the domestic market and actively explored foreign markets.Up to now, we have provided high-quality products and services to more than 1,000 customers in various industries, including: electronics and electrical appliances, medical, food, automotive electronics, optoelectronic communications, photovoltaic new energy, water treatment, transportation and other industries.
Samtion chemical supplies engineering plastics and special modified materials of S-Plastics and other brands.Our authentic products are guaranteed, with complete qualifications and superior supply capacity and price advantages.
Every batch of our products is subject to strict quality inspection to ensure the original supply. All products have MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificates!!
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
SS-Plastics Ultem STM1600.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|