S-Plastics Xenoy 1402B resin is Blowmoldable, unreinforced PC/polyester alloy. Characterized by high melt viscosity/strength with excellent low temperature impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 68 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1990 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 534 | J/m | ASTM D 256 |
| Modified Gardner, 23°C | 44 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 96 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Specific Volume | 0.84 | cm³/g | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.9 - 1.1 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.9 - 1.1 | % | S-Plastics Method |
| Source GMD, last updated:01/05/2000 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 95 - 100 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.01 - 0.02 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature (Parison) | 240 - 250 | °C |
| Barrel - Zone 1 Temperature | 235 - 245 | °C |
| Barrel - Zone 2 Temperature | 235 - 245 | °C |
| Barrel - Zone 3 Temperature | 235 - 245 | °C |
| Barrel - Zone 4 Temperature | 235 - 245 | °C |
| Adapter - Zone 5 Temperature | 235 - 245 | °C |
| Head - Zone 6 - Top Temperature | 235 - 245 | °C |
| Head - Zone 7 - Bottom Temperature | 235 - 245 | °C |
| Mold Temperature | 65 - 90 | °C |
| Die Temperature | 240 - 250 | °C |
| Source GMD, last updated:01/05/2000 | ||