Melt Volume Rate, MVR At 260°C/5.0 Kg: 21
Highlight:

S-Plastic flame retardant abs resin

,

flame retardant abs resin XCY620L

,

S-Plastic abs resin material

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic cycoloy
Certification: COA/ICP Test/Rohs/MSDS
Model Number: XCY620L
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Cycoloy XCY620L resin is PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 52 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 4.7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 115 % ASTM D 638
Tensile Modulus, 5 mm/min 2300 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 89 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 54 MPa ISO 527
Tensile Stress, break, 50 mm/min 51 MPa ISO 527
Tensile Strain, yield, 50 mm/min 4.5 % ISO 527
Tensile Strain, break, 50 mm/min 115 % ISO 527
Tensile Modulus, 1 mm/min 2200 MPa ISO 527
Flexural Stress, yield, 2 mm/min 83 MPa ISO 178
Flexural Modulus, 2 mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 640 J/m ASTM D 256
Izod Impact, notched, -30°C 480 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 56 J ASTM D 3763
Instrumented Impact Total Energy, -30°C 70 J ASTM D 3763
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 45 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 45 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 127 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 107 °C ASTM D 648
CTE, -40°C to 40°C, flow 7.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ASTM E 831
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, -40°C to 40°C, flow 8.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C Pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 127 °C ISO 306
Vicat Softening Temp, Rate B/120 129 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 126 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 105 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.14 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 260°C/5.0 kgf 22 g/10 min ASTM D 1238
Density 1.14 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.4 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg 21 cm³/10 min ISO 1133
Melt Viscosity, 260°C, 1500 sec-1 195 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm 35 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm 25 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Source GMD, last updated:09/24/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 95 - 105 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260 - 290 °C
Nozzle Temperature 240 - 280 °C
Front - Zone 3 Temperature 250 - 290 °C
Middle - Zone 2 Temperature 250 - 290 °C
Rear - Zone 1 Temperature 230 - 260 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 60 - 90 °C
Source GMD, last updated:09/24/2004  

 


 

For more information please download the datasheet

S-Plastic PC Flame Retardant ABS Resin Material Cycoloy XCY620L 0  S-Plastics Cycoloy XCY620L.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic PC Flame Retardant ABS Resin Material Cycoloy XCY620L 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)