High Modulus S-Plastic Cycoloy PC ABS Plastic Resin XCM851 High Heat

100KG
MOQ
*USD
Price
High Modulus S-Plastic Cycoloy PC ABS Plastic Resin XCM851 High Heat
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 260°C/5.0 Kg: 9
Highlight:

High Modulus Cycoloy PC ABS

,

Cycoloy PC ABS XCM851

,

Cycoloy abs plastic resin

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic cycoloy
Certification: COA/ICP Test/Rohs/MSDS
Model Number: XCM851
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Cycoloy XCM851 resin is High heat PC/ABS blend offering high modulus / low CTE and good practical impact


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 60 MPa ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min 35 MPa ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min 4 % ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 12 % ASTM D 638
Tensile Modulus, 5 mm/min 4750 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 108 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 4550 MPa ASTM D 790
Tensile Stress, yield, 5 mm/min 55 MPa ISO 527
Tensile Stress, break, 5 mm/min 45 MPa ISO 527
Tensile Strain, yield, 5 mm/min 4 % ISO 527
Tensile Strain, break, 5 mm/min 10 % ISO 527
Tensile Modulus, 1 mm/min 4600 MPa ISO 527
Flexural Stress, yield, 2 mm/min 100 MPa ISO 178
Flexural Modulus, 2 mm/min 4400 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 100 J/m ASTM D 256
Izod Impact, notched, -30°C 80 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 60 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 12 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 9 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 138 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 119 °C ASTM D 648
CTE, -40°C to 40°C, flow 4.1E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 5.6E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 4.1E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 5.6E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 139 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 122 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.3 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.3 - 0.5 % S-Plastics Method
Melt Flow Rate, 260°C/5.0 kgf 12 g/10 min ASTM D 1238
Density 1.3 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.2 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.01 % ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg 9 cm³/10 min ISO 1133
Source GMD, last updated:10/22/2008    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 100 - 110 °C
Drying Time 3 - 4 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 270 - 300 °C
Nozzle Temperature 260 - 290 °C
Front - Zone 3 Temperature 270 - 300 °C
Middle - Zone 2 Temperature 265 - 290 °C
Rear - Zone 1 Temperature 260 - 270 °C
Mold Temperature 60 - 100 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 30 - 80 %
Vent Depth 0.038 - 0.076 mm
Parameter    
Sheet Extrusion Value Unit
Drying Temperature 110 - 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 250 - 270 °C
Barrel - Zone 1 Temperature 195 - 205 °C
Barrel - Zone 2 Temperature 200 - 220 °C
Barrel - Zone 3 Temperature 220 - 240 °C
Barrel - Zone 4 Temperature 230 - 260 °C
Adapter Temperature 230 - 260 °C
Die Temperature 230 - 245 °C
Roll Stack Temp - Top 100 - 110 °C
Roll Stack Temp - Middle 110 - 120 °C
Roll Stack Temp - Bottom 145 - 155 °C
Source GMD, last updated:10/22/2008  

 

 


 

For more information please download the datasheet

High Modulus S-Plastic Cycoloy PC ABS Plastic Resin XCM851 High Heat 0  S-Plastics Cycoloy XCM851.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

High Modulus S-Plastic Cycoloy PC ABS Plastic Resin XCM851 High Heat 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)