S-Plastics Cycoloy HC1204HL resin is PC/ABS blend. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 126 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 128 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 102 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 22 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:09/18/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 110 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 290 | °C |
| Nozzle Temperature | 240 - 280 | °C |
| Front - Zone 3 Temperature | 250 - 290 | °C |
| Middle - Zone 2 Temperature | 250 - 290 | °C |
| Rear - Zone 1 Temperature | 230 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Source GMD, last updated:09/18/2007 | ||
For more information please download the datasheet | |
 | S-Plastics Cycoloy HC1204HL.pdf |