S-Plastics Cycoloy EXCY0125 resin is is a nonbrominated, nonchlorinated flame retardant-based PC+ABS product. It is available in WH8C270M only (white pearl) and for limited use.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 42 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2600 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2460 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 400 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 200°C/3.8 kgf | 21 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 2 | mm | UL 94 by GE |
| Source GMD, last updated:01/23/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 245 - 275 | °C |
| Nozzle Temperature | 245 - 275 | °C |
| Front - Zone 3 Temperature | 245 - 275 | °C |
| Middle - Zone 2 Temperature | 220 - 265 | °C |
| Rear - Zone 1 Temperature | 220 - 255 | °C |
| Mold Temperature | 60 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:01/23/2006 | ||
For more information please download the datasheet | |