S-Plastics Cycoloy CE1820 resin is Cycoloy Extrusion Grade, ABS + PC Blend, Low CTE, High Heat, High Impact,Extusion Thermoforming Grade
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 121 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 120 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3300 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2990 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 429 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 108 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 57 | J | ASTM D 3763 |
| Instrumented Impact Energy @ peak, -30 | 51 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, xflow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 60°C, flow | 6.6E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C 177 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.22 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.1 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.4 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 230°C/3.8 kgf | 1.5 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 260°C/5.0 kgf | 11 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:10/03/2003 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 225 - 240 | °C |
| Nozzle Temperature | 220 - 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 210 - 220 | °C |
| Rear - Zone 1 Temperature | 200 - 210 | °C |
| Mold Temperature | 70 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 230 - 270 | °C |
| Barrel - Zone 1 Temperature | 215 - 255 | °C |
| Barrel - Zone 2 Temperature | 220 - 260 | °C |
| Barrel - Zone 3 Temperature | 225 - 270 | °C |
| Adapter Temperature | 240 - 270 | °C |
| Die Temperature | 240 - 270 | °C |
| Roll Stack Temp - Top | 70 - 95 | °C |
| Roll Stack Temp - Middle | 95 - 115 | °C |
| Roll Stack Temp - Bottom | 105 - 130 | °C |
| Source GMD, last updated:10/03/2003 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy CE1820.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|