S-Plastics Faradex DS0036IC resin is a compound based on Polycarbonate resin, containing Stainless Steel Fiber, Flame Retardant. Added
features include: Non-Brominated & Non-Chlorinated Flame Retardant, High Impact, EMI / RMI Shielding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 59 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 86 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow (5) | 0.4 - 0.7 | % | S-Plastics Method |
| Density | 1.29 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Shielding Effectivness @ 3mm | 40 - 55 | dB | S-Plastics Method |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.6 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| Source GMD, last updated:2010/01/11 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 95 - 120 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/01/11 | ||
Other related products we recommend:
For more information please download the datesheet | |
 | S-Plastics Faradex DS0036IC.pdf |