ROHS S-Plastic Cycoloy PC ABS Plastic Resin XCY620H High Impact

100KG
MOQ
*USD
Price
ROHS S-Plastic Cycoloy PC ABS Plastic Resin XCY620H High Impact
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 260°C/5.0 Kg: 23
Highlight:

ROHS Cycoloy PC ABS

,

Cycoloy PC ABS XCY620H

,

S-Plastic abs plastic resin

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic cycoloy
Certification: COA/ICP Test/Rohs/MSDS
Model Number: XCY620H
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Cycoloy XCY620H resin is High Impact and High Flow PC + ABS. Ductile at low temperature and excelent property retention after heat aging and hydroytic aging

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 54 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 100 % ASTM D 638
Tensile Modulus, 5 mm/min 2400 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 89 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 54 MPa ISO 527
Tensile Stress, break, 50 mm/min 52 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5 % ISO 527
Tensile Strain, break, 50 mm/min 100 % ISO 527
Tensile Modulus, 1 mm/min 2300 MPa ISO 527
Flexural Stress, yield, 2 mm/min 85 MPa ISO 178
Flexural Modulus, 2 mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 600 J/m ASTM D 256
Izod Impact, notched, -30°C 350 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 55 J ASTM D 3763
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 45 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 45 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 130 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 109 °C ASTM D 648
CTE, -40°C to 40°C, flow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 8.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C Pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 130 °C ISO 306
Vicat Softening Temp, Rate B/120 132 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 128 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 108 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.15 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Density 1.15 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.4 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.1 % ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg 23 cm³/10 min ISO 1133
Source GMD, last updated:03/28/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 95 - 105 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260 - 290 °C
Nozzle Temperature 240 - 280 °C
Front - Zone 3 Temperature 250 - 290 °C
Middle - Zone 2 Temperature 250 - 290 °C
Rear - Zone 1 Temperature 230 - 260 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 60 - 90 °C
Source GMD, last updated:03/28/2006  

 


 

For more information please download the datasheet

ROHS S-Plastic Cycoloy PC ABS Plastic Resin XCY620H High Impact 0  S-Plastics Cycoloy XCY620H.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

ROHS S-Plastic Cycoloy PC ABS Plastic Resin XCY620H High Impact 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)