Sabic Cycoloy XCY480 resin is High flow
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 42 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2270 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2270 | MPa | ASTM D 638 |
| Flexural Stress | 73 | MPa | ASTM D 790 |
| Flexural Modulus | 2140 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 43 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 47 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 560 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 450 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 260 | J/m | ASTM D 256 |
| Multiaxial Impact | 130 | J | ISO 6603 |
| Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 0°C | 46 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 19 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 117 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 95 | °C | ASTM D 648 |
| CTE, -30°C to 80°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 129 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 118 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 118 | °C | ISO 75/Be |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 260°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.47 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 12 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 31 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:04/02/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 240 - 270 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 230 - 270 | °C |
| Middle - Zone 2 Temperature | 230 - 270 | °C |
| Rear - Zone 1 Temperature | 210 - 240 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Source GMD, last updated:04/02/2008 | ||
|
For more information please download the datasheet |
|
 |
Sabic Cycoloy XCY480.pdf |
|