S-Plastics Cycoloy EXCY0138 resin is a flame retardant, extrusion PC/ABS grade with Br- and Cl-free FR systems designed for thermal forming
applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 85 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2900 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2720 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 80 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2650 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 111 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 98 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D 648 |
| Ball Pressure Test, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 110 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 111 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/5.0 kgf | 10 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| UL Compliant, 94-5VB Rating (3)(4) | 2 | mm | UL 94 by GE |
| Source GMD, last updated:11/09/2005 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0 - 0.02 | % |
| Melt Temperature (Parison) | 225 - 250 | °C |
| Barrel - Zone 1 Temperature | 205 - 230 | °C |
| Barrel - Zone 2 Temperature | 215 - 245 | °C |
| Barrel - Zone 3 Temperature | 215 - 245 | °C |
| Barrel - Zone 4 Temperature | 220 - 250 | °C |
| Adapter - Zone 5 Temperature | 225 - 250 | °C |
| Head - Zone 6 - Top Temperature | 225 - 250 | °C |
| Head - Zone 7 - Bottom Temperature | 225 - 250 | °C |
| Mold Temperature | 65 - 90 | °C |
| Die Temperature | 240 - 250 | °C |
| Source GMD, last updated:11/09/2005 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy EXCY0138.pdf |
|