S-Plastics Cycoloy EXCY0045 resin is CYCOLOY of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm, featuring balanced properties in flow, impact and stiffness
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 105 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3500 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3300 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 97 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3450 | MPa | ISO 178 |
| Hardness, Rockwell R | 117 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 200 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 89 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/50 | 98 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 102 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.26 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.1 | % | ASTM D 570 |
| Moisture Absorption, 50% RH, 24 hrs | 0.01 | % | ASTM D 570 |
| Melt Flow Rate, 260°C/2.16 kgf | 17.5 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Source GMD, last updated:02/13/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 | °C |
| Drying Time | >4 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 275 - 300 | °C |
| Nozzle Temperature | 280 - 300 | °C |
| Front - Zone 3 Temperature | 280 - 300 | °C |
| Middle - Zone 2 Temperature | 275 - 300 | °C |
| Rear - Zone 1 Temperature | 275 - 300 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:02/13/2004 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy EXCY0045.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|