S-Plastics Cycoloy CY5000 resin is Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applications including business equipment, TV enclosures, among others
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 34 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2800 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2630 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 43 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 40 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2670 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 69 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 20 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 81 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 89 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 92 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 73 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/2.16 kgf | 34 | g/10 min | ASTM D 1238 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 30 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| Source GMD, last updated:06/15/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 75 - 80 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 270 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 230 - 270 | °C |
| Middle - Zone 2 Temperature | 220 - 260 | °C |
| Rear - Zone 1 Temperature | 200 - 230 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 50 - 70 | °C |
| Source GMD, last updated:06/15/2007 | ||
|
For more information please download the datasheet |
|
 |