S-Plastics Cycoloy CP8930 resin is High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2370 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2370 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 560 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 380 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 55 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*3 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 35 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 126 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 103 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 126 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 129 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 103 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.13 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/5.0 kgf | 16 | g/10 min | ASTM D 1238 |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.4 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 20 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:12/21/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 260 - 290 | °C |
| Nozzle Temperature | 260 - 290 | °C |
| Front - Zone 3 Temperature | 255 - 290 | °C |
| Middle - Zone 2 Temperature | 255 - 290 | °C |
| Rear - Zone 1 Temperature | 250 - 280 | °C |
| Mold Temperature | 75 - 100 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:12/21/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy CP8930.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|