S-Plastics Valox 310SE0resin is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard,switches and switch components and appliance housings.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 20 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2820 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 101 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2620 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 19 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
| Hardness, H358/30 | 105 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 22 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 200 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 3 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 4 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 165 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 74 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 162 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 71 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C to 138°C, flow | 1.31E-04 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 212 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 165 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 165 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 135 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 60 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.4 | - | ASTM D 792 |
| Specific Volume | 0.71 | cm³/g | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 1.1 - 1.8 | % | S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm | 1.5 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.9 - 1.6 | % | S-Plastics Method |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1.5 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.9 - 1.9 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 1 - 1.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.6 - 2.4 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/2.16 kgf | 8.6 | g/10 min | ASTM D 1238 |
| Density | 1.4 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.36 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Dielectric Strength, in air, 3.2 mm | 18.4 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | ASTM D 149 |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| High Voltage Arc Resistance {PLC) | 6 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 |
| Relative Permittivity, 100 Hz | 3.1 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Comparative Tracking Index, M | 100 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.71 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 30 | % | ISO 4589 |
| Source GMD, last updated:07/27/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Nozzle Temperature | 240 - 255 | °C |
| Front - Zone 3 Temperature | 245 - 260 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Mold Temperature | 50 - 75 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.025 | mm |
| Source GMD, last updated:07/27/2007 | ||
Hot-sale product(in stock)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT + glass filled: DR51, DR48, 420 420se0, 553, 508, 420HP
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Valox Plastic 310SE0.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|