S-Plastics Verton MVL36SX0 resin is a compound based on PP resin containing Long Glass Fiber and PTFE. Added features include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 116 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 133 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Multiaxial Impact | 5 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 163 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 157 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.37 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.73 | % | ISO 294 |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.01 | % | ISO 62-1 |
| Source GMD, last updated:09/15/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 215 - 220 | °C |
| Front - Zone 3 Temperature | 205 - 215 | °C |
| Middle - Zone 2 Temperature | 200 - 210 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/15/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton MVL36SX0.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|