S-Plastics Verton MX02795 resin is a compound based on Polypropylene resin containing Long Glass Fiber. Added features of this material
include: Chemically Coupled, Heat Stabilized, UV Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 117 | MPa | ASTM D 638 |
| Tensile Stress, break | 117 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.2 | % | ASTM D 638 |
| Tensile Strain, break | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8960 | MPa | ASTM D 638 |
| Flexural Stress | 158 | MPa | ASTM D 790 |
| Flexural Modulus | 6890 | MPa | ASTM D 790 |
| Tensile Stress, yield | 111 | MPa | ISO 527 |
| Tensile Stress, break | 122 | MPa | ISO 527 |
| Tensile Strain, yield | 2.1 | % | ISO 527 |
| Tensile Strain, break | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9570 | MPa | ISO 527 |
| Flexural Stress | 184 | MPa | ISO 178 |
| Flexural Modulus | 7750 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 854 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 267 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 7 | J | ASTM D 3763 |
| Multiaxial Impact | 13 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 52 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 161 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 4.46E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.34E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 158 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.21 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:05/12/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 220 - 250 | °C |
| Front - Zone 3 Temperature | 250 - 260 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Mold Temperature | 40 - 65 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:05/12/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton MX02795.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|