Sabic Valox 310 resin is Unreinforced, general purpose. Typical viscosity 5000-7000.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 300 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 117 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Gardner, 23°C | 40 | J | ASTM D 3029 |
| Modified Gardner, 23°C | 40 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 154 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 54 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C to 138°C, flow | 1.39E-04 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Specific Volume | 0.76 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.9 - 1.6 | % | SABIC Method |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1.5 - 2.3 | % | SABIC Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 1 - 1.7 | % | SABIC Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.6 - 2.4 | % | SABIC Method |
| Melt Viscosity | 600 | Pa-s | SABIC Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >4.E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 1.6 mm | 23.2 | kV/mm | ASTM D 149 |
| Dielectric Strength, in air, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 23.2 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Source GMD, last updated:01/05/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Nozzle Temperature | 240 - 255 | °C |
| Front - Zone 3 Temperature | 245 - 260 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Mold Temperature | 50 - 75 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.025 | mm |
| Source GMD, last updated:01/05/2000 | ||
Hot-sale product(in stock)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT + glass filled: DR51, DR48, 420 420se0, 553, 508, 420HP
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
Sabic Valox 310.pdf |
|