S-Plastics Xylex X8300MR resin is Mold release version of X8300
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 46 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1520 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1680 | MPa | ASTM D 790 |
| Hardness, Shore D, 10S reading | 73 | - | ASTM D 2240 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | >200 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >200 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1600 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 1121 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 95 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 96 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 79 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.04E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 96 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 80 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 265°C/2.16kg | 15 | g/10 min | ASTM D 1238 |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 15 | cm³/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Light Transmission | 88 | % | ASTM D 1003 |
| Haze | 1 | % | ASTM D 1003 |
| Refractive Index | 1.539 | - | ISO 489 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Source GMD, last updated:11/03/2004 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 65 - 75 | °C |
| Drying Time | 3 - 5 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 265 | °C |
| Nozzle Temperature | 245 - 265 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 250 | °C |
| Mold Temperature | 45 - 60 | °C |
| Back Pressure | 0.2 - 0.5 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:11/03/2004 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Xylex X8300MR.pdf |
|