REACH S-Plastic PET Resin Plastic Pellets Xylex X8303 Low processing Temperature, high flow with excellent impact

100KG
MOQ
*USD
Price
REACH S-Plastic PET Resin Plastic Pellets Xylex X8303 Low processing Temperature, high flow with excellent impact
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 265°C/2.16 Kg: 15
Processing Temperature: Low
Impact: High Flow With Excellent Impact
Highlight:

REACH resin plastic pellets

,

Xylex X8303 resin plastic pellets

,

REACH pet resin pellets

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Xylex
Certification: COA/ICP Test/Rohs/MSDS
Model Number: X8303
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Xylex X8303 resin is Low processing Temperature, high flow with excellent impact

Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 46 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 44 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 140 % ASTM D 638
Tensile Modulus, 5 mm/min 1680 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 72 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 1620 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 48 MPa ISO 527
Tensile Stress, break, 50 mm/min 43 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 140 % ISO 527
Tensile Modulus, 1 mm/min 1690 MPa ISO 527
Flexural Stress, break, 2 mm/min 72 MPa ISO 178
Flexural Modulus, 2 mm/min 1720 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 1000 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 65 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 20 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 98 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 92 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 80 °C ASTM D 648
CTE, -40°C to 40°C, flow 9.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 9.E-05 1/°C ASTM E 831
CTE, 23°C to 60°C, flow 9.2E-05 1/°C ISO 11359-2
CTE, 23°C to 60°C, xflow 9.8E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 100 °C ISO 306
Vicat Softening Temp, Rate B/120 100 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 90 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % S-Plastics Method
Melt Flow Rate, 265°C/2.16kg 32 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg 30 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze 2 % ASTM D 1003
Source GMD, last updated:12/04/2006    

 

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 70 - 80 °C
Drying Time 3 - 5 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 240 - 270 °C
Nozzle Temperature 240 - 270 °C
Front - Zone 3 Temperature 240 - 270 °C
Middle - Zone 2 Temperature 235 - 265 °C
Rear - Zone 1 Temperature 235 - 255 °C
Mold Temperature 50 - 70 °C
Screw Speed 20 - 100 rpm
Source GMD, last updated:12/04/2006  

 


 

  
 
 

For more information please download the datasheet

REACH S-Plastic PET Resin Plastic Pellets Xylex X8303 Low processing Temperature, high flow with excellent impact 0  S-Plastics Xylex X8303.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

REACH S-Plastic PET Resin Plastic Pellets Xylex X8303 Low processing Temperature, high flow with excellent impact 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)