S-Plastics Xylex X8409 resin is PC + Polyester, Injection Molding or Injection/Extrusion Blow Molding Grade, Chemical Resistance and Transparency
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 92 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min | 2230 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2220 | MPa | ASTM D 790 |
Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5.8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 117 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2180 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 89 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C | 854 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C | 72 | J | ASTM D 3763 |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -10°C | 8 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 123 | °C | ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 116 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 104 | °C | ASTM D 648 |
CTE, -40°C to 40°C, flow | 1.04E-04 | 1/°C | ASTM E 831 |
CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 102 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
Density | 1.2 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 265°C/2.16 kg | 3 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Light Transmission | 88 | % | ASTM D 1003 |
Haze | 1.5 | % | ASTM D 1003 |
Refractive Index | 1.576 | - | ASTM D 542 |
Source GMD, last updated:08/05/2004 |
Processing
Parameter | ||
Extrusion Blow Molding | Value | Unit |
Drying Temperature | 75 - 90 | °C |
Drying Time | 4 - 6 | hrs |
Drying Time (Cumulative) | 24 | hrs |
Maximum Moisture Content | 0.01 - 0.02 | % |
Melt Temperature (Parison) | 250 - 270 | °C |
Barrel - Zone 1 Temperature | 235 - 260 | °C |
Barrel - Zone 2 Temperature | 235 - 260 | °C |
Barrel - Zone 3 Temperature | 235 - 260 | °C |
Barrel - Zone 4 Temperature | 235 - 260 | °C |
Adapter - Zone 5 Temperature | 235 - 260 | °C |
Head - Zone 6 - Top Temperature | 240 - 270 | °C |
Head - Zone 7 - Middle Temperature | 240 - 270 | °C |
Head - Zone 7 - Bottom Temperature | 240 - 270 | °C |
Mold Temperature | 30 - 75 | °C |
Source GMD, last updated:08/05/2004 |
For more information please download the datasheet |
|
S-Plastics Xylex X8409.pdf |
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
Click to consult and get the latest quotation within 24 hours! |