Sabic Xylex EXXY0008 resin is Opaque PC+polyester alloy. High flow, chemical resistant/good mechanical properties. UV-stabilized. Exc
weatherability.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 39 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 39 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1310 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 52 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1440 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 854 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 85 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 60 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 57 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.1 | - | ASTM D 792 |
| Melt Flow Rate, 266°C/5.0 kgf | 32 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:03/01/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 30 - 50 | °C |
| Drying Time | 3 - 5 | hrs |
| Drying Time (Cumulative) | 7 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 265 | °C |
| Nozzle Temperature | 230 - 265 | °C |
| Front - Zone 3 Temperature | 230 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 250 | °C |
| Mold Temperature | 25 - 55 | °C |
| Back Pressure | 0.2 - 0.5 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:03/01/2002 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
Sabic Xylex EXXY0008.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|