S-Plastics Xylex EXXY0005 resin is WILL BE COMMERCIALIZED AS X8001EX. Unreinforced, PC+polyester alloy for extrusion applications.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, break, 50 mm/min | >200 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 1800 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 77 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -10°C | 5 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 105 | °C | ASTM D 1525 |
Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/120 | 105 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 89 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Melt Flow Rate, 265°C/2.16kg | 12 | g/10 min | ASTM D 1238 |
Density | 1.17 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 265°C/2.16 kg | 11 | cm³/10 min | ISO 1133 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 17 | cm³/10 min | ISO 1133 |
Source GMD, last updated:06/18/2001 |
Other related products we recommend:
For more information please download the datasheet |
|
![]() |
S-Plastics Xylex EXXY0005.pdf |
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|