Features
Specifications
Melt Flow Rate, 265°C/2.16kg: 7
Impact Modified: Yes
Ductility: Good
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Xylex
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXXX0087
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Xylex EXXX0087 resin is Impact modified Xylex with good ductility for eyewear frames, mobile phone housings etc


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 49 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 53 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min >150 % ASTM D 638
Tensile Modulus, 5 mm/min 1700 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 75 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 1790 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 48 MPa ISO 527
Tensile Stress, break, 50 mm/min 44 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5 % ISO 527
Tensile Strain, break, 50 mm/min 130 % ISO 527
Tensile Modulus, 1 mm/min 1700 MPa ISO 527
Flexural Stress, yield, 2 mm/min 72 MPa ISO 178
Flexural Modulus, 2 mm/min 1750 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 900 J/m ASTM D 256
Izod Impact, notched, -30°C 700 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 68 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 68 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 84 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed 99 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 87 °C ASTM D 648
CTE, -40°C to 40°C, flow 8.7E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 8.4E-05 1/°C ASTM E 831
Vicat Softening Temp, Rate B/120 105 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 82 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.3 - 0.4 % S-Plastics Method
Melt Flow Rate, 265°C/2.16kg 11 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg 12 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 86 % ASTM D 1003
Source GMD, last updated:11/02/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 65 - 80 °C
Drying Time 3 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 270 °C
Nozzle Temperature 250 - 270 °C
Front - Zone 3 Temperature 250 - 270 °C
Middle - Zone 2 Temperature 245 - 270 °C
Rear - Zone 1 Temperature 245 - 260 °C
Mold Temperature 45 - 60 °C
Back Pressure 0.1 - 0.5 MPa
Screw Speed 20 - 100 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.013 - 0.02 mm
Source GMD, last updated:11/02/2006  

 

 
 
Other related products we recommend:
 

For more information please download the datasheet

S-Plastic Xylex EXXX0087 Impact Modified Xylex With Good Ductility For Eyewear Frames, Mobile Phone Housings Etc 0  S-Plastics Xylex EXXX0087.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Xylex EXXX0087 Impact Modified Xylex With Good Ductility For Eyewear Frames, Mobile Phone Housings Etc 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)