Sabic Xylex EXXX0053 UV 400 nm cut for sunglasses lens or other optical applications

100KG
MOQ
*USD
Price
Sabic Xylex EXXX0053 UV 400 nm cut for sunglasses lens or other optical applications
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 265°C/2.16kg: 10
Optical Application: UV 400 Nm Cut For Sunglasses Lens Or Other
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Xylex
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXXX0053
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Xylex EXXX0053 resin UV 400 nm cut for sunglasses lens or other optical applications


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 56 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 59 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.8 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 105 % ASTM D 638
Tensile Modulus, 5 mm/min 2200 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 92 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2050 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 64 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 132 % ISO 527
Tensile Modulus, 1 mm/min 2160 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2120 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 790 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 71 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 9 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 126 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 119 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 107 °C ASTM D 648
CTE, -40°C to 40°C, flow 1.04E-04 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 1.04E-04 1/°C ASTM E 831
CTE, 23°C to 60°C, flow 9.E-05 1/°C ISO 11359-2
CTE, 23°C to 60°C, xflow 9.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/120 127 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 106 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.6 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 265°C/2.16kg 12 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg 10 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 86 % ASTM D 1003
Haze 1.5 % ASTM D 1003
Source GMD, last updated:02/20/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 65 - 80 °C
Drying Time 3 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 270 °C
Nozzle Temperature 250 - 270 °C
Front - Zone 3 Temperature 250 - 270 °C
Middle - Zone 2 Temperature 245 - 270 °C
Rear - Zone 1 Temperature 245 - 260 °C
Mold Temperature 45 - 60 °C
Back Pressure 0.1 - 0.5 MPa
Screw Speed 20 - 100 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.013 - 0.02 mm
Source GMD, last updated:02/20/2006  

 
 
Other related products we recommend:
 

For more information please download the datasheet

Sabic Xylex EXXX0053 UV 400 nm cut for sunglasses lens or other optical applications 0  Sabic Xylex EXXX0053.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Xylex EXXX0053 UV 400 nm cut for sunglasses lens or other optical applications 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)