S-Plastics Xylex EXXX0021 resin is Visual Effects, impact modified PC+Polyester alloy. Telecom. Color package may affect performance.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 140 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1550 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 48 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 103 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 83 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/25/2003 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 65 - 80 | °C |
| Drying Time | 3 - 5 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 250 - 270 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 270 | °C |
| Rear - Zone 1 Temperature | 245 - 260 | °C |
| Mold Temperature | 45 - 60 | °C |
| Back Pressure | 0.1 - 0.5 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:08/25/2003 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xylex EXXX0021.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|