S-Plastics Xylex EXXX0005 resin is PRELIMINARY DATA. PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1760 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 83 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1880 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | >150 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 71 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 854 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 94 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 90 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 85 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.19E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 8.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 44 | g/10 min | ASTM D 1238 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 42 | cm³/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Light Transmission | 88 | % | ASTM D 1003 |
| Haze | 2 | % | ASTM D 1003 |
| Source GMD, last updated:02/19/2002 |
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
For more information please download the datasheet | |
| S-Plastics Xylex EXXX0005.pdf |
Get The Latest Quotation |