S-Plastics Xylex resin is a copolymer of transparent polycarbonate (PC) and amorphous polyester. Compared with PC, adding polyester to xylex resin provides enhanced chemical resistance against certain fluids and improves the stress cracking resistance of the resin.
●Characteristics
1,Excellent combination of clarity and weatherability
2,Excellent combination of clarity and chemical resistance
3,Excellent flo
S-Plastics Xylex resin X7300 is a PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 52 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min | 1840 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 83 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 1940 | MPa | ASTM D 790 |
Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | >150 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 71 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C | 660 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C | 95 | J | ASTM D 3763 |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 108 | °C | ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 102 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 |
CTE, -40°C to 40°C, flow | 1.15E-04 | 1/°C | ASTM E 831 |
CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E 831 |
CTE, 23°C to 60°C, flow | 8.5E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | S-Plastics Method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
Melt Flow Rate, 265°C/2.16kg | 21 | g/10 min | ASTM D 1238 |
Density | 1.18 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 265°C/2.16 kg | 21 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Light Transmission | 88 | % | ASTM D 1003 |
Haze | 2 | % | ASTM D 1003 |
Source GMD, last updated:08/25/2005 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 80 - 95 | °C |
Drying Time | 3 - 5 | hrs |
Drying Time (Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 250 - 270 | °C |
Nozzle Temperature | 250 - 270 | °C |
Front - Zone 3 Temperature | 250 - 270 | °C |
Middle - Zone 2 Temperature | 245 - 265 | °C |
Rear - Zone 1 Temperature | 240 - 250 | °C |
Mold Temperature | 45 - 60 | °C |
Back Pressure | 0.2 - 0.5 | MPa |
Screw Speed | 20 - 100 | rpm |
Shot to Cylinder Size | 40 - 80 | % |
Vent Depth | 0.013 - 0.02 | mm |
Source GMD, last updated:08/25/2005 |
For more information please download the datasheet |
|
S-Plastics Xylex PC/PET X7300.pdf |