SabikXylex Pemanfaatan bahan kimiaresin adalahPC + POLYESTER paduan tidak diperkuat. aliran tinggi, tahan kimia, UV-stabil. untuk digunakan dalam aplikasi oftalmik
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1840 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 83 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1940 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 150 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1900 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 71 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 854 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 94 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 108 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 93 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 88 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.19E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 60°C, aliran | 8.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 106 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode SABIC |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode SABIC |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 21 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/07/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 65 - 80 | °C |
| Waktu Pengeringan | 3 - 5 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 290 | °C |
| Suhu Nozzle | 250 - 290 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 245 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 255 | °C |
| Suhu Cetakan | 45 - 60 | °C |
| Tekanan Belakang | 0.2 - 0.5 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:09/07/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
Sabic Xylex EXXX0043.pdf |
|