SabikXylex X8303 resin adalah suhu pengolahan rendah, aliran tinggi dengan dampak yang sangat baik
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 44 | MPa | ASTM D 638 |
Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 140 | % | ASTM D 638 |
Tensile Modulus, 5 mm/min | 1680 | MPa | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 72 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1620 | MPa | ASTM D 790 |
Tekanan tarik, hasil, 50 mm/menit | 48 | MPa | ISO 527 |
Tekanan tarik, pecah, 50 mm/menit | 43 | MPa | ISO 527 |
Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
Tekanan tarik, putus, 50 mm/menit | 140 | % | ISO 527 |
Modulus tarik, 1 mm/menit | 1690 | MPa | ISO 527 |
Tekanan lentur, istirahat, 2 mm/menit | 72 | MPa | ISO 178 |
Flexural Modulus, 2 mm/menit | 1720 | MPa | ISO 178 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, bertanduk, 23°C | 1000 | J/m | ASTM D 256 |
Energi Total Dampak Instrumen, 23°C | 65 | J | ASTM D 3763 |
Izod Impact, bernotas 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1A |
Termal | Nilai | Satuan | Standar |
Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ASTM D 1525 |
HDT, 0,45 MPa, 3,2 mm, tidak diiris | 92 | °C | ASTM D 648 |
HDT, 1,82 MPa, 3,2 mm, tidak diiris | 80 | °C | ASTM D 648 |
CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 |
CTE, 23°C sampai 60°C, aliran | 9.2E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C sampai 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temperature, Tingkat B/50 | 100 | °C | ISO 306 |
Vicat Softening Temperature, Tingkat B/120 | 100 | °C | ISO 306 |
HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 90 | °C | ISO 75/Af |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
Tingkat Aliran Peleburan, 265°C/2,16kg | 32 | g/10 menit | ASTM D 1238 |
Kepadatan | 1.2 | g/cm3 | ISO 1183 |
Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 30 | cm3/10 menit | ISO 1133 |
Optik | Nilai | Satuan | Standar |
Transmisi Cahaya | 88 | % | ASTM D 1003 |
Kabut | 2 | % | ASTM D 1003 |
Sumber GMD, terakhir diperbarui:12/04/2006 |
Pengolahan
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 70 - 80 | °C |
Waktu Pengeringan | 3 - 5 | jam |
Kandungan Kelembaban Maksimal | 0.02 | % |
Suhu Peleburan | 240 - 270 | °C |
Suhu Nozzle | 240 - 270 | °C |
Suhu depan - Zona 3 | 240 - 270 | °C |
Tengah - Zona 2 Suhu | 235 - 265 | °C |
Bagian belakang - Zona 1 Suhu | 235 - 255 | °C |
Suhu Cetakan | 50 - 70 | °C |
Kecepatan sekrup | 20 - 100 | rpm |
Sumber GMD, terakhir diperbarui:12/04/2006 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
S-Plastics Xylex X8303.pdf |