Melt Volume Rate, MVR At 265°C/2.16 Kg: 21
UV-Stabilized: Yes
Chemical Resistance: Good
Applications: Ophthalmic
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Xylex
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXXX0043
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Xylex EXXX0043 resin is PC+POLYESTER unreinforced alloy. High flow, chemically resistant,UV-stabilized. For use in ophthalmic applications


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 51 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 150 % ASTM D 638
Tensile Modulus, 50 mm/min 1840 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 83 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 1940 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 55 MPa ISO 527
Tensile Stress, break, 50 mm/min 55 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5 % ISO 527
Tensile Strain, break, 50 mm/min >150 % ISO 527
Tensile Modulus, 1 mm/min 1900 MPa ISO 527
Flexural Stress, break, 2 mm/min 71 MPa ISO 178
Flexural Modulus, 2 mm/min 2000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 854 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 94 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 9 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 108 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 93 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 88 °C ASTM D 648
CTE, -40°C to 40°C, flow 1.19E-04 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 1.04E-04 1/°C ASTM E 831
CTE, 23°C to 60°C, flow 8.5E-05 1/°C ISO 11359-2
CTE, 23°C to 60°C, xflow 8.5E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/120 106 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 90 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % SABIC Method
Density 1.18 g/cm³ ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg 21 cm³/10 min ISO 1133
Source GMD, last updated:09/07/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 65 - 80 °C
Drying Time 3 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 290 °C
Nozzle Temperature 250 - 290 °C
Front - Zone 3 Temperature 250 - 290 °C
Middle - Zone 2 Temperature 245 - 280 °C
Rear - Zone 1 Temperature 245 - 255 °C
Mold Temperature 45 - 60 °C
Back Pressure 0.2 - 0.5 MPa
Screw Speed 20 - 100 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.013 - 0.02 mm
Source GMD, last updated:09/07/2004  

 
 
Other related products we recommend:
 

For more information please download the datasheet

Sabic Xylex EXXX0043 PC+POLYESTER Unreinforced Alloy High Flow Chemically Resistant UV-Stabilized ophthalmic application 0  Sabic Xylex EXXX0043.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Xylex EXXX0043 PC+POLYESTER Unreinforced Alloy High Flow Chemically Resistant UV-Stabilized ophthalmic application 1Click to consult and get the latest quotation within 24 hours!

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)