S-Plastics Verton ZF3021 resin is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic,
Flame Retardant.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 127 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 132 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 152 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.1 - 0.6 | % | S-Plastics Method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+13 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 1.6 mm | 27.2 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 3.2 mm | 17.5 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:09/08/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 275 - 295 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 255 - 265 | °C |
| Mold Temperature | 60 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/08/2008 |