S-Plastics Verton PF006I resin is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 142 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 97 | MPa | ASTM D 638 |
| Tensile Strain, break | 3.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 8.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 16230 | MPa | ASTM D 638 |
| Flexural Stress | 211 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 157 | MPa | ASTM D 790 |
| Flexural Modulus | 6550 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6820 | MPa | ASTM D 790 |
| Tensile Stress, break | 138 | MPa | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 35 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 99 | MPa | ISO 527 |
| Tensile Strain, break | 8.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9650 | MPa | ISO 527 |
| Flexural Stress | 148 | MPa | ISO 178 |
| Flexural Modulus | 6510 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 727 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 16 | J | ASTM D 3763 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D 648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.35 | - | ASTM D 792 |
| Density | 1.35 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.83 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.9 - 2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.11 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.62 - 0.67 | % | ISO 294 |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.83 | % | ISO 62 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |